OPAQUE MBS IMPACT MODIFIER MB-300
DESCRIPTION
MB-300 is a ternary co-polymer with core-shell structure consisted of Methyl Methacrylate, 1,3-Butadiene and Styrene. Its main function is to improve impact strength in indoor applications, especially for PVC finished products which have higher impact strength needs. In addition, it can lengthen production cycle due to excellent metal release.
KEY PROPERTY
• Excellent improved impact property
• Excellent thermal ability
• Easy dispersion
• Wide processing window
PRODUCT INDEX
Item | Specification |
Appearance | White, free flowing powder |
Bulk Density, g/cm3 | 0.45±0.10 |
Sieve residue (30 mesh), % | ≤ 2.0 |
Volatile content, % | ≤ 1.20 |
DYNAMIC THERMAL STABILITY COMPARISON
Test condition: double-roller mill temperature190℃ Thickness: 0.5mm
YI at different time Test standard: ASTM E313-00
Type | 3' | 5' | 7' | 9' | 11' | 13' | 15' |
1# Competitor | 0.94 | 3.10 | 4.47 | 5.34 | 6.55 | 7.91 | 8.93 |
2# MB-300 | 0.99 | 3.61 | 4.22 | 5.88 | 7.05 | 8.00 | 9.14 |
MECHANICAL PROPERTY COMPARISON
Pat impact: -5℃stable 20min， 25.020HZ pat 15s
Type | Thickness(mm) | Number of all samples | Number of damaged samples |
1# Competitor | 0.5±0.02 | 10 | 1 |
2# MB-300 | 0.5±0.02 | 10 | 0 |
TENSILE STRENGTH COMPARISON
Test standard: GBT 1040-2006 Test condition: 23℃ 10mm/min
Type | Tensile strength (MPa) | Elongation at break (%) |
1# Competitor | 39.66±0.35 | 161.47±6.35 |
2# MB-300 | 41.79±0.30 | 181.25±5.40 |
STORAGE
The product should be stored in cool and dry surroundings.
The shelf life is two years, it can be still used if qualified by inspection after shelf life.
PACKAGE
25kg/bag with PP bag or customized packaging according to customer requirements.
LOADING CAPACITY
For 20GP container, we can load 8.8mt with pallets or 10mt without pallets.
For 40HC container, we can load 20.8mt with pallets or 25mt without pallets.
OPAQUE MBS IMPACT MODIFIER MB-300
DESCRIPTION
MB-300 is a ternary co-polymer with core-shell structure consisted of Methyl Methacrylate, 1,3-Butadiene and Styrene. Its main function is to improve impact strength in indoor applications, especially for PVC finished products which have higher impact strength needs. In addition, it can lengthen production cycle due to excellent metal release.
KEY PROPERTY
• Excellent improved impact property
• Excellent thermal ability
• Easy dispersion
• Wide processing window
PRODUCT INDEX
Item | Specification |
Appearance | White, free flowing powder |
Bulk Density, g/cm3 | 0.45±0.10 |
Sieve residue (30 mesh), % | ≤ 2.0 |
Volatile content, % | ≤ 1.20 |
DYNAMIC THERMAL STABILITY COMPARISON
Test condition: double-roller mill temperature190℃ Thickness: 0.5mm
YI at different time Test standard: ASTM E313-00
Type | 3' | 5' | 7' | 9' | 11' | 13' | 15' |
1# Competitor | 0.94 | 3.10 | 4.47 | 5.34 | 6.55 | 7.91 | 8.93 |
2# MB-300 | 0.99 | 3.61 | 4.22 | 5.88 | 7.05 | 8.00 | 9.14 |
MECHANICAL PROPERTY COMPARISON
Pat impact: -5℃stable 20min， 25.020HZ pat 15s
Type | Thickness(mm) | Number of all samples | Number of damaged samples |
1# Competitor | 0.5±0.02 | 10 | 1 |
2# MB-300 | 0.5±0.02 | 10 | 0 |
TENSILE STRENGTH COMPARISON
Test standard: GBT 1040-2006 Test condition: 23℃ 10mm/min
Type | Tensile strength (MPa) | Elongation at break (%) |
1# Competitor | 39.66±0.35 | 161.47±6.35 |
2# MB-300 | 41.79±0.30 | 181.25±5.40 |
STORAGE
The product should be stored in cool and dry surroundings.
The shelf life is two years, it can be still used if qualified by inspection after shelf life.
PACKAGE
25kg/bag with PP bag or customized packaging according to customer requirements.
LOADING CAPACITY
For 20GP container, we can load 8.8mt with pallets or 10mt without pallets.
For 40HC container, we can load 20.8mt with pallets or 25mt without pallets.