MBS IMPACT MODIFIER MB-200
DESCRIPTION
MB-200 is a type of transparent MBS impact modifier. It has dual benefits with balance of mechanical properties and optical properties. It is environmentally friendly and mainly used to produce clear PVC sheet and film with balance of transparency and impact strength.
KEY PROPERTY
• Promote fusion
• Balance of transparency and impact strength
• Good heat stability
• Improve melt flow ability
PRODUCT INDEX
Item | Specification |
Appearance | White, free flowing powder |
Bulk Density, g/cm3 | 0.40±0.10 |
Sieve residue (30 mesh), % | ≤ 2.0 |
Volatile content, % | ≤ 1.00 |
BASIC FORMULA FOR THE FOLLOWING TESTS
Ingredients | 0# Control | 1# Competitor | 2# MB-200 |
PVC(K-57) | 100.00 | 100.00 | 100.00 |
Tin stabilizer | 1.20 | 1.20 | 1.20 |
Transparent processing aid P-20 | 1.00 | 1.00 | 1.00 |
Int. lubricant G-60 | 1.00 | 1.00 | 1.00 |
Ext. lubricant G-74 | 0.50 | 0.50 | 0.50 |
MBS Competitor | -- | 5.00 | -- |
MB-200 | -- | -- | 5.00 |
FUSION PROPERTY COMPARISON
Test conditions | 160℃ 60rpm | ||||
| |||||
Type | Fusion time (S) | Highest torque (Nm) | Lowest torque (Nm) | Equilibrium torque (Nm) | |
1# Competitor | 41 | 43.3 | 20.3 | 22.3 | |
2#MB-200 | 37 | 46.0 | 23.5 | 22.4 | |
Test conditions | 190℃ 30rpm | ||||
| |||||
Type | Fusion time (S) | Highest torque (Nm) | Lowest torque (Nm) | Equilibrium torque (Nm) | |
1# Competitor | 41 | 30.9 | 23.7 | 16.6 | |
2# MB-200 | 37 | 33.0 | 27.3 | 16.4 | |
Test conditions | 190℃ 60rpm | ||||
| |||||
Type | Fusion time (S) | Highest torque (Nm) | Lowest torque (Nm) | Equilibrium torque (Nm) | |
1# Competitor | 21 | 36.5 | 24.8 | 15.6 | |
2# MB-200 | 16 | 39.2 | 31.0 | 15.6 | |
OPTICAL PROPERTY COMPARISON
Type | Haze |
1# Competitor | 4.02±0.04 |
2# MB-200 | 3.85±0.03 |
DYNAMIC THERMAL STABILITY COMPARISON
Test condition: double-roller mill temperature190℃ Thickness: 0.5mm
YI at different time Test standard: ASTM E313-00
Type | 3' | 5' | 7' | 9' | 11' | 13' | 15' |
1# Competitor | 0.95 | 3.20 | 4.57 | 5.68 | 6.67 | 7.85 | 8.90 |
2# MB-200 | 0.99 | 3.58 | 4.24 | 5.98 | 7.08 | 8.01 | 9.17 |
MECHANICAL PROPERTY COMPARISON
Pat impact: 5℃ stable 20min， 25.020HZ pat 15s
Type | Thickness(mm) | Number of all samples | Number of damaged samples |
0# Control | 0.5±0.02 | 10 | 10 |
1# Competitor | 0.5±0.02 | 10 | 1 |
2# MB-200 | 0.5±0.02 | 10 | 0 |
-5℃stable 20min， 25.020HZ pat 15s
Type | Thickness(mm) | Number of all samples | Number of damaged samples |
0# Control | 0.5±0.02 | 10 | 10 |
1# Competitor | 0.5±0.02 | 10 | 2 |
2# MB-200 | 0.5±0.02 | 10 | 1 |
TENSILE STRENGTH COMPARISON
Test standard: GBT 1040-2006 Test condition: 23℃ 10mm/min
Type | Tensile strength (MPa) | Elongation at break (%) |
0# Control | 46.71±0.24 | 115.64±4.12 |
1# Competitor | 45.20±0.43 | 157.04±3.54 |
2# MB-200 | 45.24±0.46 | 164.89±4.51 |
METAL RELEASE PROPERTY COMPARISON
Test condition: Double-roller mill temperature 196℃
Type | Sticking time(S) |
0# Control | 340±10 |
1# Competitor | 504±12 |
2# MB-200 | 513±12 |
STORAGE
The product should be stored in cool and dry surroundings.
The shelf life is two years, it can be still used if qualified by inspection after shelf life.
PACKAGE
25kg/bag with PP bag or customized packaging according to customer requirements.
LOADING CAPACITY
For 20GP container, we can load 8.8mt with pallets or 10mt without pallets.
For 40HC container, we can load 20.8mt with pallets or 25mt without pallets.
MBS IMPACT MODIFIER MB-200
DESCRIPTION
MB-200 is a type of transparent MBS impact modifier. It has dual benefits with balance of mechanical properties and optical properties. It is environmentally friendly and mainly used to produce clear PVC sheet and film with balance of transparency and impact strength.
KEY PROPERTY
• Promote fusion
• Balance of transparency and impact strength
• Good heat stability
• Improve melt flow ability
PRODUCT INDEX
Item | Specification |
Appearance | White, free flowing powder |
Bulk Density, g/cm3 | 0.40±0.10 |
Sieve residue (30 mesh), % | ≤ 2.0 |
Volatile content, % | ≤ 1.00 |
BASIC FORMULA FOR THE FOLLOWING TESTS
Ingredients | 0# Control | 1# Competitor | 2# MB-200 |
PVC(K-57) | 100.00 | 100.00 | 100.00 |
Tin stabilizer | 1.20 | 1.20 | 1.20 |
Transparent processing aid P-20 | 1.00 | 1.00 | 1.00 |
Int. lubricant G-60 | 1.00 | 1.00 | 1.00 |
Ext. lubricant G-74 | 0.50 | 0.50 | 0.50 |
MBS Competitor | -- | 5.00 | -- |
MB-200 | -- | -- | 5.00 |
FUSION PROPERTY COMPARISON
Test conditions | 160℃ 60rpm | ||||
| |||||
Type | Fusion time (S) | Highest torque (Nm) | Lowest torque (Nm) | Equilibrium torque (Nm) | |
1# Competitor | 41 | 43.3 | 20.3 | 22.3 | |
2#MB-200 | 37 | 46.0 | 23.5 | 22.4 | |
Test conditions | 190℃ 30rpm | ||||
| |||||
Type | Fusion time (S) | Highest torque (Nm) | Lowest torque (Nm) | Equilibrium torque (Nm) | |
1# Competitor | 41 | 30.9 | 23.7 | 16.6 | |
2# MB-200 | 37 | 33.0 | 27.3 | 16.4 | |
Test conditions | 190℃ 60rpm | ||||
| |||||
Type | Fusion time (S) | Highest torque (Nm) | Lowest torque (Nm) | Equilibrium torque (Nm) | |
1# Competitor | 21 | 36.5 | 24.8 | 15.6 | |
2# MB-200 | 16 | 39.2 | 31.0 | 15.6 | |
OPTICAL PROPERTY COMPARISON
Type | Haze |
1# Competitor | 4.02±0.04 |
2# MB-200 | 3.85±0.03 |
DYNAMIC THERMAL STABILITY COMPARISON
Test condition: double-roller mill temperature190℃ Thickness: 0.5mm
YI at different time Test standard: ASTM E313-00
Type | 3' | 5' | 7' | 9' | 11' | 13' | 15' |
1# Competitor | 0.95 | 3.20 | 4.57 | 5.68 | 6.67 | 7.85 | 8.90 |
2# MB-200 | 0.99 | 3.58 | 4.24 | 5.98 | 7.08 | 8.01 | 9.17 |
MECHANICAL PROPERTY COMPARISON
Pat impact: 5℃ stable 20min， 25.020HZ pat 15s
Type | Thickness(mm) | Number of all samples | Number of damaged samples |
0# Control | 0.5±0.02 | 10 | 10 |
1# Competitor | 0.5±0.02 | 10 | 1 |
2# MB-200 | 0.5±0.02 | 10 | 0 |
-5℃stable 20min， 25.020HZ pat 15s
Type | Thickness(mm) | Number of all samples | Number of damaged samples |
0# Control | 0.5±0.02 | 10 | 10 |
1# Competitor | 0.5±0.02 | 10 | 2 |
2# MB-200 | 0.5±0.02 | 10 | 1 |
TENSILE STRENGTH COMPARISON
Test standard: GBT 1040-2006 Test condition: 23℃ 10mm/min
Type | Tensile strength (MPa) | Elongation at break (%) |
0# Control | 46.71±0.24 | 115.64±4.12 |
1# Competitor | 45.20±0.43 | 157.04±3.54 |
2# MB-200 | 45.24±0.46 | 164.89±4.51 |
METAL RELEASE PROPERTY COMPARISON
Test condition: Double-roller mill temperature 196℃
Type | Sticking time(S) |
0# Control | 340±10 |
1# Competitor | 504±12 |
2# MB-200 | 513±12 |
STORAGE
The product should be stored in cool and dry surroundings.
The shelf life is two years, it can be still used if qualified by inspection after shelf life.
PACKAGE
25kg/bag with PP bag or customized packaging according to customer requirements.
LOADING CAPACITY
For 20GP container, we can load 8.8mt with pallets or 10mt without pallets.
For 40HC container, we can load 20.8mt with pallets or 25mt without pallets.